Predicting the strengths of date fiber reinforced concrete subjected to elevated temperature using artificial neural network, and Weibull distribution

Date palm fiber (DPF) is normally used as fiber material in concrete. Though its addition to concrete leads to decline in durability and mechanical strengths performance. Additionally, due to its high ligno-cellulose content and organic nature, when used in concrete for high temperature application, the DPF can easily degrade causing reduction in strength and increase in weight loss. To reduce these effects, the DPF is treated using alkaline solutions. Furthermore, pozzolanic materials are normally added to the DPF composites to reduce the effects of the ligno-cellulose content. Therefore, in this study silica fume was used as supplementary cementitious material in DPF reinforced concrete (DPFRC) to reduce the negative effects of elevated temperature. Hence this study aimed at predicting the residual strengths of DPFRC enhanced/improved with silica fume subjected to elevated temperature using different models such as artificial neural network (ANN), multi-variable regression analysis (MRA) and Weibull distribution. The DPFRC is produced by adding DPF in proportions of 0%, 1%, 2% and 3% by mass. Silica fume was used as partial substitute to cement in dosages of 0%, 5%, 10% and 15% by volume. The DPFRC was then subjected to elevated temperatures between 200 and 800 °C. The weight loss, residual compressive strength and relative strengths were measured. The residual compressive strength and relative strength of the DPFRC declined with addition of DPF at any temperature. Silica fume enhanced the residual and relative strengths of the DPFRC when heated to a temperature up to 400 °C. To forecast residual compressive strength (RCS) and relative strength (RS), we provide two distinct ANN models. The first layer's inputs include DPF (%), silica fume (%), temperature (°C), and weight loss (%). The hidden layer is thought to have ten neurons. M-I is the scenario in which we use RCS as an output, whereas M-II is the scenario in which we use RS as an output. The ANN models were trained using the Levenberg–Marquardt backpropagation algorithm (LMBA). Both neural networking models exhibit a significant correlation between the predicted and actual values, as seen by their respective R = 0.99462 and R = 0.98917. The constructed neural models M-I and M-II are highly accurate at predicting RCS and RS values. MRA and Weibull distribution were used for prediction of the strengths of the DPFRC under high temperature. The developed MRA was found to have a good prediction accuracy. The residual compressive strength and relative strength followed the two-parameter Weibull distribution.

www.nature.com/scientificreports/use of neural networking is treated as best prediction scheme like in order to semantically segment concrete crack images, Dung 26 suggested a crack detection system based on deep Fully Convolutional Networks (FCN).The backbone of the FCN encoder, three alternative pre-trained network architectures, were tested for image classification on a public concrete fracture.The average precision achieved by the FCN network is around 90%.The suggested technique for concrete fracture detection was validated using images taken from a film of a cyclic loading test on a concrete specimen.The evaluation of crack density and the reasonable detection of cracks were both shown to be accurate.A deep neural network model was proposed by Nguyen, Kashani 27 to forecast the compressive strength of foamed concrete.To enhance the performance of the deep neural network model, a new, high-order neuron was created.Moreover, the rectified linear unit activation function and cross-entropy cost function were used to improve the model's performance.Moreover, using a particular data set, the current model was used for predicting the compressive strength of foamed concrete.The findings were then compared with those of other machine learning techniques, such as the Conventional Artificial Neural Network (C-ANN) and Second-Order Artificial Neural Network (SO-ANN).The results showed that density, followed by the waterto-cement and sand-to-cement ratios, had a significant impact on the compressive strength of foamed concrete.The proposed model can assist scientists and engineers in the mixture design optimization of foamed concrete by offering a trustworthy prediction tool.To forecast the compressive strength of rubber concrete, Ly, Nguyen 28 presented a novel Deep Neural Network model generation process.In order to achieve this, a rubber concrete database was meticulously created, comprising a set of input parameters for the binder, aggregate, and other relevant concrete variables, while the compressive strength was taken into account as an output.A statistical study of the model's prediction outputs is combined with a thorough analysis of the number of hidden layers and the neurons in each layer as part of the creation of the DNN model.The findings demonstrate that, in terms of a number of well-known performance indicators, including coefficient of determination, root mean square error, and mean absolute error, the DNN model outperforms conventional neural network topologies.Also, the proposed DNN model displays higher prediction accuracy than results from earlier publications that used other machine learning algorithms from the literature.The DNN algorithm underwent a sensitivity study utilizing partial dependence plots in order to thoroughly examine the impact of each individual input variable on the anticipated compressive strength of rubber concrete.Using Response Surface Methodology (RSM) and Artificial Neural Networks (ANN) techniques, Kursuncu, Gencel 29 investigated the effects of Waste Marble Powder (WMP) and Rice Husk Ash (RHA) partially substituting fine aggregate and cement into Foam Concrete (FC) on compressive and flexural strength, porosity, and thermal conductivity coefficient.In the experimental design, the WMP and RHA parameters were determined as three levels, while the foam parameter was calculated as two levels.It was discovered that the ANN technique worked well for estimating the answers.It was discovered that the RSM method worked well for both estimating responses and figuring out the efficient parameters.The recent studies in this regard can be accessed in Refs [30][31][32] .
Based on the existing study, there are scanty literature that used ANN to predict the properties of silica fume modified DPFRC under high temperature.Hence, in this study ANN was used to predict the residual compressive strength and relative strength of the DPFRC exposed to high temperature condition.Additionally, multivariable regression and Weibull distribution were used for statistical analysis and establishing models for estimating the compressive strengths of the DPFRC concrete under high temperature and carry out reliability analysis of the concrete under elevated temperature.

Materials
Silica fume and Portland cement were the binder materials employed in this study.The cement conformed with ASTM C150/C150M 33 specifications.The physical and chemical properties of the binder materials are summarized in Table 1.Natural sand with a maximum size of 4.75 mm in Saturated Surface-Dried (SSD) condition was utilized as the fine aggregate.As revealed in Fig. 1, the fine aggregate has a well graded gradation.Natural crushed gravel with maximum size of 19 mm and in SSD condition was used as the coarse aggregate.Similarly, from Fig. 1, the coarse aggregate was found to be well graded.The physical properties of the aggregates are summarized in Table 2.
DPF was adopted as a fiber material in this study.The fiber was collected from a neighboring farm in its raw state as shown in Fig. 2a.The raw fiber was obtained in the shape of a quadrilateral mesh of length varying between 300 and 500 mm, and width between 200 to 300 mm.To process the raw fiber for use in concrete, the mesh was fully immersed in clean water for about 2 h, after which it was washed severally with water.An alkaline solution (3% NaOH) was prepared, and the washed fiber was fully immersed in it and kept for 3 h.This treatment was carried out to remove all the excess impurities and dirt from the fiber surface which cannot be removed with normal water and make the fiber surface rougher.After the soaking period, the DPF was cleansed thoroughly using water and then air dried for about 48-72 h until it is completely dried.After drying, the fiber was separated and cut into a single fiber length between 20 and 30 mm and diameters between 0.2 and 1.0 mm as shown in Fig. 2b.This final product of the DPF was used as a natural fiber in concrete.

Mix Proportioning
The processed DPF was added at varying amounts of 0%, 1%, 2% and 3% by mass of cementitious materials to the concrete.The design of the concrete mix was carried out using the absolute volume method highlighted in ACI 211.1R 34 .Cement was partially replaced with silica fume in the mixes.The dosages of replacements were 0%, 5%, 10% and 15% by volume of cement.To address the effect of variation in water-to-binder ratio in the concrete, a polycarboxylate based water reducing admixture (superplasticizer) was added.The dosage of the admixture was 1% by weight of binder materials in all the mixes.The mixes were produced using the different dosages of silica  3.These mixes were prepared and cast in the laboratory for testing.From Table 3, each of the mixes were given a unique ID based on its content of DPF and silica fume.For illustration, mix M2D0S is the mix containing 2% DPF and 0% silica fume, while mix M3D5S is the mix made with 3% DPF and 5% silica fume, and mix M1D15S is the mix containing 1% DPF and 15% silica fume.

Samples preparations
The developed mix proportions were produced in the laboratory for testing.Each of the constituent material for the mix under consideration was weighed.The batching, mixing, and casting of the concrete samples were accomplished following the procedures outlined in ASTM C192/C192M 21 .The cement used was also ensured to be free from agglomeration, impurity, and lumps.A rotating drum mixer type available in the laboratory was used   www.nature.com/scientificreports/for mixing the fresh concrete.The fine aggregate, silica fume and cement were emptied to the mixer, they were then thoroughly mixed for about 45 secs.The DPF and part of the mixing water combined with superplasticizer were added gradually while mixing was going on.The coarse aggregate and remaining part of water combined with superplasticizer were added.The mixing progressed and was stopped after a completely homogenous mix was obtained.The ready mixed concrete in the mixer is shown in Fig. 3a.The freshly mixed concrete was then poured into the 100 mm cube molds which were tight, cleaned, and oiled.The concrete in the cubes were kept in the laboratory for 24 h to settle and hardened.The hardened concrete in the mold is presented in Fig. 3b.After hardening, they were removed from the molds and submerged in clean water for curing.

Test methods
The cube samples were removed from the curing tank after 28 days curing period and air dried for at least 24 h to make them completely dry.The samples were then weighed, and the weight was recorded as W i .The samples were subjected to elevated temperature by placing them inside an electric furnace.Each of the mixes was heated at varying temperatures of 24 °C 200 °C, 400 °C, 600 °C and 800 °C for 2 h exposure periods in the electric furnace as shown in Fig. 4a.The heating was done at a fixed rate of 10 °C/min till the chosen temperature is attained, and then allowed to undergo heating at a constant temperature for 2 h.After heat exposure duration is attained, the furnace was turned off and kept closed for the samples to cool completely inside.After cooling, the samples were weighed again, and the weight was recorded as W F .Equation (1) was then used to calculate weight loss.The heated cube samples were then subjected to compressive strength test with the aid of a universal testing machine of 2000 kN capacity following the methods elaborated in BS EN 12,390-3 35 as shown in Fig. 4b.The relative strengths of each mix were then calculated using Eq.(2).

Neural networking model
Use of neural networking models to make predictions is considered by various researchers in different research scenarios [36][37][38][39] .Owing to such a directory we offer two different neural networking models to make prediction of Residual Compressive Strength (RCS) and Relative Strength (RS).In detail, neural network is composed of three different layers.Four different inputs, namely date palm fiber, temperature, silica fume, and weight loss are considered in the first layer.The hidden layer owns 10 neurons and case-wise outputs are taken in the last layer.M-I is the case when we take RCS as an output while M-II is the case when we carried RS as an output.
The selection of inputs and outputs are offered in Table.4.  Tan-Sig transfer function (Eq. 3) is used in hidden layer while Purelin transfer function (Eq.4) is used in the output layer.Regression and mean square error relations are mathematically expressed as Eqs.( 5) and ( 6) as follows:

Experimental results
The results of the weight loss, residual compressive strength, and relative strengths of the DPF reinforced concrete containing silica fume as supplementary cementitious material presented in Table 5 was based on the previous studies by Adamu, Ibrahim 40 , and has been reported in this study to enhance readability and ease of understanding the findings in this study based on the ANN, Weibull distribution and multivariable regression analysis models developed.The weight loss of the DPFRC intensified with rise in temperature which was due to the loss of capillary water and gels from the microstructure of the concrete.At higher temperatures of 600 °C and above, the weight loss was due to evaporation of chemically bound water from the hydration products.Furthermore, there was an escalation in weight loss with increment in percentage addition of DPF to the concrete.This was because DPF creates more voids in the concrete, therefore under high temperature capillary water and chemically bound water evaporates easily from the voids, thereby escalating the weight loss in the DPFRC.The partial substitution www.nature.com/scientificreports/ of cement with silica fume in the DPFRC decreased the weight loss when heated up to a temperature of 400 °C.This is due to the pozzolanic reaction between the silica fume and cement hydration products which densified the concrete microstructure and prevent the evaporation of water from the concrete under high temperature 40,41 .
The strengths of the DPFRC improved when subjected to elevated temperature of up to 400 °C regardless of the proportions of DPF and silica fume in the mixes.This improvement in strength can be linked to the formation of excess tobermorite from the hydrothermal reactions between the SiO 2 from silica fume and calcium oxide from cement.The addition of DPF to the concrete resulted in reduction in residual and relative strengths of the concrete due to premature failure occurring in the concrete due to voids created by the DPF in the microstructure of the concrete.Additionally, the poor adhesion between the DPF and cement paste also caused a reduction in strengths at any temperature.The strengths of the DPFRC improved with partial replacement of not more than 10% cement with silica fume at a temperature of up to 600 °C.The improvement in strength might be due to the consumption of excess Portlandites (Ca(OH) 2 ) thereby inhibiting its conversion to lime at high temperature, hence avoiding the damage that can be caused by this reaction 40,41 .

Neural networking analysis
Both RCS and RS are predicted by using ANN models namely M-I and M-II respectively.Figures 6a, 7b are the ultimate training performance outcomes for ANN models.In detail, Fig. 6a gives performance pattern for neural networking to predict the RCS and Fig. 6b gives the performance pattern for neural networking to predict the RS.From Fig. 6a one can see that the mean square error is high at the initial stage while for upcoming epochs the error reduces significantly.We have seen that the best validation performance for the model M-I is 0.000305017 at epoch 16.
From Fig. 6b, one can see that for the first 4 epochs the mean square error is high.For higher epochs the error significantly reduces to desired values.The best validation performance for the model M-II is 0.0044732 at epoch 47. Figure 7a

Statistical modelling using multivariable regression
A statistical modelling using multivariable regression analysis (MRA) was carried out to establish model equations for calculating or forecasting the properties of the DPFRC exposed to elevated temperature using DPF, silica fume and temperature as the inputs.
The basic globalized MRA equation is expressed in form of linear equation expressed as Eq. ( 7) 42 .
For which y denotes the response/output, Ψ is the coefficient of the intercept, Ζ is the linear regression coefficients.
However, as most of the relationships between the responses/outputs and variables contains some curvature, non-linear multi-variable regression analysis using second-order polynomial will improve the prediction accuracy and reduce the errors in the models.The global second-order non-linear MRA equation is expressed as Eq. ( 8) 42 .
where y stands for the response/output, x stands for the independent variables, Ζ i represents the coefficient of the 1st order polynomial in the equations, and Ζ ij represents the coefficient of the 2nd order polynomial in the equation, n is the number of input variables, and Ψ is the constant of regression.
In this research, the non-linear MRA was employed to develop models for forecasting and calculating the strengths and weight loss for the DPFRC concrete exposed to high temperature.

ANOVA for developed models
The developed mathematical equations for the prediction of the weight loss, residual compressive strength and relative strength of the DPFRC containing silica fume under elevated temperature is given as Eqs.( 9)-( 11) respectively.( 7)  www.nature.com/scientificreports/ In the above Eqs, W L represents the weight loss in %, Fc and RC are the residual and relative compressive strengths respectively, in MPA and % respectively.T is temperature in °C, D is DPF in %, and S is silica fume in %.
Table 8 highlights the ANOVA for all the models established for the estimation of the DPFRC's properties under high temperature.Using the level of significance (P < 0.05), the statistical significance for all the models were checked.All the models were found to be statistically significant based on the significance test (P < 0.05), as their P-values are less than 0.05.Hence the statistical null hypotheses for all the models were false and rejected.In terms of R 2 , higher values of R 2 clarified the high degree of correlation of the models with the experimental results and hence high predicting accuracy.From Table 8, the weight loss model has an excellent R 2 value of 0.928 which is very close to 1, and hence the model is said to have a very high accuracy and prediction.For the residual and relative strength models, their R 2 values of 0.818 and 0.786 are said to be very good and also close to 1, and hence the models have good correlation and prediction ability.all models can be said to have excellent R 2 scores which is ≥ 0.9.Further model accuracy test was done by comparing the standard errors (SE) for each model relative to its mean square values.The low SE relative to mean square for each of the model explains the accuracy of prediction with less errors.

Diagnostic plots
The normal probability graphs for the weight loss, residual compressive strength and residual strength models are presented as Fig. 11a-c, respectively.All the models a reasonably good correlation with the straight trend line drawn on its plot.Therefore, the experimental data and the models for the DPFRC containing silica fume under high temperature all followed and agreed with the normal probability distribution.By comparing the normal plots of the models, it can be clearly seen that the residual compressive strength model (Fig. 11b) has the best fit with its straight trend line, and hence is said to be the most normally distributed model.
Figure 12 highlights the predicted values against the experimental data graphs for the DPFRC models modified with silica fume exposed to elevated temperature.The weight loss model has the highest fitness between its predicted and actual values with R 2 of 0.93 as seen in Fig. 12a.The relative strength model has the least fitness between its predicted and actual values when compared to the other models, with an R 2 of 0.79.From the plots only about 7%, 18% and 21% of the total data for the weight loss, residual compressive strength and relative strength models respectively were not perfectly fitted with the developed mathematical models.Consequently, the proposed models for predicting or forecasting the weight loss and strengths of the DPFRC containing silica fume under high temperature can be said to have a reasonably good to high prediction accuracy.

Weibull distribution function
Weibull distribution is a numerical approach that is normally used by engineers for the analysis of brittle materials failure.Several research outcomes reveal that the Weibull distribution parameters are linked with the sizes and types of flaws 43 .In addition, Weibull statistical analysis can also be used to analyse quasi-brittle materials 44 .
The fracture toughness and strengths of quasi brittle materials like rocks followed the Weibull distribution., where the two and three parameters Weibull distribution functions were utilized for analysing the rock fracture's probability 44,45 .Concrete is considered as a quasi-brittle composite material due to variation in its strength and other mechanical properties which are dependent on the type and quantity of cementitious materials, aggregate type and strength, temperature and humidity, casting and curing methods.Therefore, concrete's strength and other properties can be analysed using Weibull distribution 43 .Previous research has adopted Weibull distribution for the analysis of concrete's properties.He and Xie 46 analysed the compressive and tensile strengths of concrete using Weibull distribution and reported a very high correlation for the models where the concrete strengths obeyed the two-parameter Weibull distribution function.Kencanawati, Iizasa 47 used Weibull distribution for the analysis of the strengths and reliability of recycled aggregate concrete (RAC).They found a good correlation between the Weibull analysis and mechanical strengths of the concrete and concluded that the Weibull distribution can be used for reliability analysis of the RAC.The dynamic and static mechanical properties of FRC have been evaluated using Weibull distribution statistical method and was reported to have a high prediction and correlation 48,49 .The drop weight impact resistance test on concrete was analysed statistically using Weibull distribution functions 48,50 .The Weibull distribution was found to be a suitable statistical analysis method for impact and fatigue tests on concrete due to its nature of enhancing hazard function, which characterize the real behaviour of engineering constructions under repeated loads 51 .Zheng, Cheng 52 modified the Weibull distribution to a simplified form with lesser parameters and containing the pre-peak and post-peak stresses in shotcrete.They found that that the modified Weibull distribution model effectively quantified the failure mechanism of the shotcrete, and the Weibull model was reasonably in good correlation with the experimental data, with the model having an acceptable reliability.Guo, Qiao 53 used the two and three parameters Weibull distributions to carryout stochastic analysis for the assessment of concrete structure's durability.They found that the Weibull distribution is well fitted for the analysis of the life data and durability of the concrete structures throughout its service life.The three parameters Weibull distribution model has the best fit compared to the two parameters Weibull distribution.Shahraki, Hua 54 employed Weibull distribution to establish probabilistic models for predicting the residual compressive strengths of calcareous and siliceous concrete when exposed to temperature between 200 to 1000 °C for 2 h exposure.They defined the parameters of the Weibull distribution as a function of temperature in continuous closed-form solutions.Their findings showed that the model for the residual compressive strength followed the Weibull distribution, and the model can be employed for computational and analytical frameworks.The cumulative probability function of the Weibull distribution W(N) is used for the estimation and prediction of the residual compressive strength and relative strengths of the DPFRC subjected to elevated temperature as presented in Eq. ( 12) below 55 .By integrating Eq. ( 12), the random variable distribution function F(W P ) is derived as presented in Eq. ( 13).
In Eqs. ( 12) and ( 13), γ and Ζ denotes the shape parameter and characteristic life (scale factor) respectively, for the Weibull distribution, T represents the definite value of the random variable W, Ζ 0 is the parameter of the location for which Ζ ≥ Ζ 0 and T ≥ Ζ 0.
Supposing the minimum concrete life Ζ 0 = 0 for the compressive strengths of the DPFRC under high temperature, then the survival probability function F(S P ) can be presented as Eq. ( 14).Now simplifying Eq. ( 14) by taking natural log of both sides twice returned Eq. ( 15) Lastly, Eq. ( 15) can be utilized for checking if the compressive strengths of the DFPRC mixes exposed to high temperature followed the two-parameter Weibull distribution function, which is carried out by solving the Eq. ( 15) above and then relating it with the normal straight-line equation (Y = Mx + C) to get γ, γLn(Ζ) and γLn(T).From the expression the degree of correlation (R 2 ) of the line can also be obtained and used to explain the accuracy of the Weibull distribution 50 .
In the above Eq.( 16), M represents the strength loss order number of the residual or relative compressive strength after subjecting to high temperature, rearranged in rising order, N represents the number of mixes of the DFPRC.
Due to the fact that subjecting concrete to elevated temperature will increase its quasi-brittle nature and causes further variation in its strength, this study utilized the Weibull distribution function for the probabilistic modelling and reliability analysis of DPFRC containing silica fume under elevated temperatures.

Analysis of compressive strengths of DPFRC using Weibull distribution
The residual compressive strength (Fc) and relative strengths (Rc) of the DPFRC modified with silica fume exposed to elevated temperatures between 200 and 800 °C was analysed using Weibull distribution.The Weibull distribution parameters is presented in Table 9 and is used to plots the Weibull plots and find the coefficient of determination (R 2 ).The plots of Ln(Ln(1/P J ) against Ln(Fc) is presented as Fig. 13a, while the graph of Ln(Ln(1/ P J ) against Ln(Rc) is given as Fig. 13b.The ANOVA for the Weibull distribution analysis is given in Table 10.From Fig. 13a,b, the Weibull charts for all the strengths demonstrates and followed a linear pattern with a very high R 2 s superior to 0.93.Hence, the residual compressive strength and relative strength of the DFPRC when exposed to elevated temperature followed the two-parameter Weibull distribution 56,57 .Hence the Weibull distribution function can be used for evaluation of the reliability or failure probability of the DPFRC under high temperatures.Shahraki, Hua 54 have also found a similar result, where they reported the residual compressive strength of calcareous and siliceous concrete at temperature up to 1000 °C followed the two-parameter Weibull distribution function.

The Anderson-darling test hypotheses
The Anderson-Darling test (AD-value) and p-value were used to test if the residual compressive strength and residual strengths followed the normal probability distribution.The AD statistical values was calculated based on the following equations [58][59][60] .( 12)  where n = sample size, F(X) = cumulative distribution function for the specified distribution and i = the i th sample when the data is sorted in ascending order The AD statistical values for the residual and relative strengths were plotted as shown in Fig. 14a,b respectively.The Probability (P-values) were then calculated using the formulas obtained from R.B. D' Augostino and M.A. Stephens, Eds., 1986 61 and summarized in Table 11.From Table 11, the P values for both the residual compressive

Reliability analysis
The compressive strengths of the DPFRC under high temperature followed the two-parameter Weibull distribution as obtained in Sect.3.2.3.Hence Weibull analysis was implemented for the estimation of the residual compressive strength and relative strengths of the DPFRC which corresponds to different survival probability (reliability).Equation ( 17) is used to estimate the different failure probabilities which correspond to the residual compressive strengths and relative strengths of the DPFRC.
In the above equation, Fc and Rc represents the residual compressive strength and relative strength respectively, P f represents probability of failure, Ζ and γ denotes the scale factor and shape factor respectively 57 .
Finally, the survival probability or design reliability (S P ) is obtained using Eq. ( 18) Table 12 presents the design residual compressive strength and residual strengths for the DPFRC under elevated temperature at different survival probabilities.The survival probabilities for the compressive strengths of the DPFRC are plotted and presented in Fig. 15a,b.The design life of the DPFRC should be selected in such a way that only a small probability that loss in compressive strength will occur under high temperature.From Fig. 15, as the survival probability increases both the residual compressive strength and relative strength decrease and vice versa.From Table 12 for instance, at 99% failure probability (1% survival probability), the design residual compressive strength and relative strengths are 3.05 MPa and 7.39% respectively.This implies that about 99% of the DPFRC mixes can survive subjecting to a temperature of up to 800 °C for 2 h duration without failure and still achieve a compressive strength of 3.05 MPa.Similarly, at 10% failure probability (90% survival probability), the design residual compressive strength and relative strength are 56.10MPa and 149.51% respectively.Meaning, that about 10% of the DPFRC mixes can survive exposure to elevated temperature up to 800 °C for 2 h and still achieve a residual compressive strength up to 56.10 MPa without failure.

Conclusions
From the findings of the experimental results and analysis in this study.The following conclusions arises.• The addition of DPF led to reduction in the residual compressive strength and relative strengths of the DPFRC, while the replacement of up to 10% cement with silica fume resulted to improvement in the residual compressive strength and relative strength of the DPFRC when subjected to a temperature up to 400 °C.• The best validation performance for the model M-I is 0.000305017 at epoch 16 while for the model M-II is 0.0044732 at epoch 47.
• For neural networking model M-I, most of the predictive values carry errors in-between − 0.02 to + 0.02, which seems acceptable.• The maximum predictive values by neural networking model M-II, carry error within bandwidth of − 0.05 to + 0.05 • For predictive neural model M-I, the regression is noticed R = 0.995 while for neural model M-II, the regres- sion value is R = 0.989.Both depict the strong correlation between predicted and actual values.• The multivariable regression models established for forecasting the performance of DPFRC exposed to high temperature have a very high statistical significance with a very good degree of correlation.• The compressive strengths of the DPFRC concrete containing silica fume exposed to elevated temperature follows the two-parameter Weibull distribution functions.• From the reliability analysis about 10% of the DFPRC mixes can survive exposure to elevated temperature up to 800 °C for 2 h and still achieve a compressive strength and relative strength up to 56.10 MPa and 149.51% respectively without failure.
For future works, the ANN techniques can be employed for the prediction of the mechanical properties and durability performance of PW concrete modified with GNP under normal environmental conditions.Additionally, the ANN techniques can be utilized for the prediction of the durability properties of the PW concrete modified with GNP subjected to other environmental conditions such as acid attack, salt or chloride attack, freeze and thaw.

Figure 1 .
Figure 1.Particle Size distribution of aggregates.

Figure 2 .
Figure 2. DPF used in this study.

Figure 5
offers the design of artificial neural networking model to predict the Residual Compressive Strength (RCS) and Relative Strength (RS).Training of model is done by using 195 sample of both RCS and RS towards(1)

Figure 6 .
Figure 6.(a) Training performance outcomes for M-I.(b) Training performance outcomes for M-II.
gives the error histogram for ANN model to predict RCS and Fig. 7b gives the error histogram for ANN model to predict RS.One can see that the training of neural working model is finished reasonably.
Figure 8a offers the error bar for the predictive values of RCS with targeted values of RCS while Fig. 8b gives the error bar for the predictive values of RS with its targeted values.In detail, from Fig. 8a one can see that the error values from mean line are not far away.Most of the predictive values carry errors in between − 0.02 to + 0.02 which seems acceptable.Some values carry errors within the band range of − 0.04 to + 0.04.Out of 195 sample values only four predictive values carry error within range of − 0.08 to + 0.08.In Fig. 8b, we can see that maximum predictive values carry error within bandwidth of − 0.05 to + 0.05.Out of 195 samples values only 05 values carry error in between − 0.15 to + 0.15.The regression plots for both neural networking models are offered in Fig. 9a,b.In detail, Fig. 9a offers the regression outcome for ANN model constructed to predict the RCS while Fig. 9b gives the regression outcome for ANN model constructed to predict the RS.It is important to note that (a) (b)

Table 1 .
Properties of binders.

Table 5 .
40sults of weight loss and strengths of DPFRC under high temperature40.

Table 6 .
Characteristics of neural networking model, M-I.

Table 7 .
Characteristics of neural networking model, M-II.

Table 8 .
ANOVA summary for multivariable regression models.

Table 10 .
ANOVA for regression coefficients of Weibull distributions.

Table 11 .
P-values obtained from AD test.strength and relative strength are very low (less than 0.05), hence the P-values of the AD statistic is not significant, hence the data does not follow the normal distribution.Therefore, Weibull distribution analysis which was used for the statistical analysis of the residual compressive strength and relative strength of the DPFRC subjected to high temperature is more appropriate.

Table 12 .
Residual and relative strength at different survival probability.